Rajammal, K. and Kufian, M.Z. and Majid, S.R. and Arof, Abdul Kariem (2009) Synthesis and characterization Of LiNi1_xZnxV04 4. In: National Workshop on Functional Materials 2009, 16 June 2009, Centre for Ionics,University of Malaya.
![[img]](http://eprints.um.edu.my/style/images/fileicons/application_pdf.png)
|
PDF
synthesis_and_characterization.pdf - Published Version Download (1MB) |
Abstract
LiNil-xZnxV04 was synthesized at x = 0.0, 0.2, 0.4 and 0.8. by a polymer hybrid sol gel method. In this work acetates of lithium (C2H302Li), nickel (C2H302Ni) and zinc (C2H302Zn) with ammonium metavanadate (NH4V03) were used to synthesize t~e samples. These materials were dissolved in distilled water, stirred and heated continuously until a clear green solution was obtained. At this stage, a solution of chitosan in 1% acetic acid was added. The solution was continuously stirred and heated until it dried. The obtained precursor powder was sintered at 700°C for 3 hours. The crystallite size, lattice constant and surface morphology has been studied for zinc substituted LiNiV04. X-ray diffraction (XRD) exhibits peaks without impurities. Zinc substituted LiNiV04 shows decreasing crystallite size from x =' 0.0 to X = 0.4. Crystallite size increases again from x = 0.4 to x = 0.8. Cyclic voltammetric (CV) studies were performed.
| Item Type: | Conference or Workshop Item (Paper) |
|---|---|
| Funders: | UNSPECIFIED |
| Uncontrolled Keywords: | Substitution, cathode materials, sol-gel method |
| Subjects: | T Technology > TA Engineering (General). Civil engineering (General) |
| Divisions: | Faculty of Science > Department of Physics |
| Depositing User: | Mr. Mohd Samsul Ismail |
| Date Deposited: | 18 Dec 2014 00:43 |
| Last Modified: | 04 Oct 2018 06:08 |
| URI: | http://eprints.um.edu.my/id/eprint/11182 |
Actions (login required)
 |
View Item |