Ali, A.H. and Shuhaimi, A. and Hassan, Z. and Yusoff, Y. (2013) Compositional and structural characterization of Heterostructure InGaN-based light-emitting diode by high resolution x-ray diffraction. Advanced Materials Research, 620. pp. 22-27. DOI https://doi.org/10.4028/www.scientific.net/AMR.620.22.
PDF
00011485_86654.pdf Restricted to Repository staff only Download (353kB) |
Abstract
This paper focuses on the compositional and structural characterization of InGaN-based light-emitting diode (LED) using high resolution x-ray diffraction (HRXRD) system. The LED was epitaxially grown on Si (111) substrate that comprises of In0.11Ga0.89N multi-quantum-well (MQW) active layer. Phase analysis 2θ-scan proved the composition of GaN (0002) and (0004) at 34.63o and 72.98o,respectively. Rocking curve φ-scan showed six significant peaks of the hexagonal GaN structures with consistent angular gaps of ~60o. From x-ray rocking curve (XRC) ω-scan, screw and mix dislocation density is found as 2.85 × 109 cm-2, while pure edge dislocation density is found as 2.23 × 1011 cm-2.
Item Type: | Article |
---|---|
Funders: | UNSPECIFIED |
Uncontrolled Keywords: | InGaN; Light-emitting diode; X-ray diffraction; Multi-quantum-well. |
Subjects: | Q Science > Q Science (General) Q Science > QC Physics |
Divisions: | Faculty of Science > Department of Physics |
Depositing User: | Ms. Norhamizah Tamizi |
Date Deposited: | 28 Apr 2014 02:17 |
Last Modified: | 28 Apr 2014 02:17 |
URI: | http://eprints.um.edu.my/id/eprint/9782 |
Actions (login required)
View Item |