Naderi, Nima and Ahmad, Harith (2024) Performance stability of porous silicon solar cells using reduced graphene oxide for applications in harsh environments. Optics Communications, 559. p. 130422. ISSN 0030-4018, DOI https://doi.org/10.1016/j.optcom.2024.130422.
Full text not available from this repository.Abstract
The impact of graphene on the photovoltaic stability of solar cells made of porous silicon (PSi) is discussed in this research. Here, reduced graphene oxide (rGO) capping layers electrophoretically deposited on PSi substrates were used to regulate the photoluminescence (PL) quenching of the PSi substrates. The samples' morphology showed that after graphene transfer, the porosity structure remained unaltered, and rGO layers completely covered the PSi surface. The rGO layers were successfully deposited on PSi substrates, according to the Raman analysis of the rGO/PSi, which revealed two prominent peaks corresponding to the G and D graphene bands. Additionally, the D-mode intensity was higher than the G-band intensity, showing that the deposited rGO layers had fewer structural defects and irregularities. The stability of the optical properties of PSi substrates was tested by comparing the PL spectra before and after graphene deposition. The findings demonstrated that the PL quenching of rGO-capped PSi structure was mitigated even after prolonged exposure to laser light. Therefore, the optical consistency of PSi samples was enhanced through deposition of graphene layers. Then, bare and rGOcovered PSi substrates were used to fabricate heterojunction solar cells, and their current-voltage results were measured under a solar light simulator at various temperatures. The optoelectrical tests showed that the availability of unstable species, such as hydrogen bonds on the PSi surface, caused a reduction in the efficiency of bare PSi devices at high temperatures. These terminations changed due to temperature changes, which decreased the photovoltaic performance of PSi substrates. This deterioration was moderated when graphene was transferred, which improved the photovoltaic stability of PSi-based solar cells. The rGO capping layer increased the electrical stability of fabricated solar cell based on PSi substrate during temperature changes.
| Item Type: | Article |
|---|---|
| Funders: | Ministry of Higher Education, Malaysia [HiCoE Grant (PRC-2022)], Universiti Malaya, Malaysia (BKS002-2023); (IIRG001A-2023), Materials & Energy Research Center (MERC) (491400007) |
| Uncontrolled Keywords: | Reduced graphene oxide; Photovoltaic stability; Porous silicon; PL quenching |
| Subjects: | Q Science > Q Science (General) Q Science > QC Physics |
| Divisions: | Faculty of Science > Department of Physics Deputy Vice Chancellor (Research & Innovation) Office > Photonics Research Centre |
| Depositing User: | Ms. Juhaida Abd Rahim |
| Date Deposited: | 28 Oct 2024 08:21 |
| Last Modified: | 28 Oct 2024 08:21 |
| URI: | http://eprints.um.edu.my/id/eprint/45550 |
Actions (login required)
 |
View Item |