Azhar, N.E.A. and Mamat, M.H. and Abu Bakar, Ahmad Shuhaimi and Shariffudin, S.S. and Rusop, M. (2021) Synthesis of Anatase Titanium Dioxide Nanotube Arrays via Electrochemical Anodization. Lecture Notes in Mechanical Engineering, 46. pp. 677-685. ISSN 21954356, DOI https://doi.org/10.1007/978-981-15-9505-9_61.
Full text not available from this repository.Abstract
Titanium dioxide (TiO2) nanotube arrays (NTAs) material have received attention due to their high stability in optoelectronic devices. As-prepared TiO2 nanotubes layers are amorphous and their properties are not sufficient enough to applied in device applications. The TiO2 NTAs was synthesized by electrochemical anodization method. The medium was mixed to facilitate the growth of TiO2 NTAs and annealed to improve the anatase structure. The field emission scanning electron microscopy (FESEM) images revealed the prepared TiO2 NTAs grow uniformly with average diameter 50.82 nm (450 °C) and 68.17 nm (as-prepared sample). The Raman spectroscopy reported the annealing temperature is critical issue to determine the crystallinity and structure of TiO2. The X-ray diffraction pattern showed the TiO2 NTAs exhibit anatase phase with prominent (101) diffraction peak that was recorded for the sample annealed at 450 °C. The band gap value (3.21 eV) was obtained for the sample annealed at 450 °C due to homogeneity of the TiO2 NTAs structures. This approach is cost-effective in synthesizing high quality ordered of TiO2 NTAs for optoelectronic applications. © 2021, The Author(s), under exclusive license to Springer Nature Singapore Pte Ltd.
| Item Type: | Article |
|---|---|
| Funders: | UNSPECIFIED |
| Uncontrolled Keywords: | Annealing temperature; Anodization; TiO2 NTAs |
| Subjects: | Q Science > Q Science (General) Q Science > QC Physics |
| Divisions: | Faculty of Science Faculty of Science > Department of Physics |
| Depositing User: | Ms Zaharah Ramly |
| Date Deposited: | 27 Nov 2023 11:39 |
| Last Modified: | 29 Nov 2023 04:06 |
| URI: | http://eprints.um.edu.my/id/eprint/36002 |
Actions (login required)
 |
View Item |