Zakaria, N.A. and Yahya, S.Y.S. and Isa, M.I.N. and Mohamed, N.S. and Subban, R.H.Y. (2009) Conductivity and dynamic mechanical studies of PVC/PEMA blend polymer electrolytes. In: International Conference on Functionalized and Sensing Materials, 07-09 Dec 2009, Bangkok, Thailand. (Submitted)
![[img]](http://eprints.um.edu.my/style/images/fileicons/application_pdf.png)
|
PDF
Conductivity_and_Dynamic_Mechanical.pdf - Submitted Version Download (3MB) |
Abstract
The ionic conductivity and mechanical properties of poly (vinyl chloride) (PVC)/poly (ethyl methacrylate) (PEMA) polymer blends containing LiN(CF3S03h as doping salt has been studied using electrical impedance spectroscopy (EIS) and Dynamic Modulus Analysis (DMA) as a function of polymer blend ratios and lithium salt concentration. The film with PVC/PEMA composition of 65 :35 obtained the highest conductivity with good transparency. DMA showed that both the storage modulus (E') and the glass transition temperature (Tg) of the PVC/PEMA is increased with PEMA concentration. In the case of PVC/PEMA-LiN(CF3S02)2 films, the conductivity was found to increase with concentration of salt added with a maximum in conductivity at 35 wt.% LiN(CF3S02h. The Tg values of the doped films was found to increase with concentration of salt such that the film with the highest conductivity value has the highest Tg.
| Item Type: | Conference or Workshop Item (Paper) |
|---|---|
| Funders: | UNSPECIFIED |
| Subjects: | T Technology > TP Chemical technology |
| Depositing User: | Mr. Mohd Samsul Ismail |
| Date Deposited: | 17 Dec 2014 02:42 |
| Last Modified: | 17 Dec 2014 02:42 |
| URI: | http://eprints.um.edu.my/id/eprint/11123 |
Actions (login required)
 |
View Item |