Teoh, Min Wei and Ng, Chui Kim and Lee, Kit Yee Sara and Singh, Ramesh and Ting, Chen Hunt and Chuah, Yea Dat and Lim, Yuze Ignatius and Tan, Chou Yong and Yeo, Wei Hong (2023) Synthesis and Characterization of Chicken Bone-Derived Hydroxyapatite Incorporating Pectin. Chemical Engineering & Technology, 46 (12, SI). pp. 2504-2512. ISSN 0930-7516, DOI https://doi.org/10.1002/ceat.202300019.
Full text not available from this repository.Abstract
Hydroxyapatite (HA) was synthesized from chicken bone waste by calcination. Pectin was extracted from orange peels by microwave irradiation, and 1 and 3 wt % of pectin was incorporated into the HA. The resulting powders were then pressed into disk samples before being sintered at temperatures of 1050, 1150, and 1250 degrees C for 2 h. Various analytical techniques, including Fourier transform infrared spectroscopy, X-ray diffraction, scanning electron microscopy, density measurement, and Vickers microhardness tests, were used to evaluate the characteristics and mechanical properties of the samples. The incorporation of pectin did not interfere with the pure phases of HA, and minimal amounts of beta-tricalcium phosphate were detected in the XRD patterns. Both ball milling and the addition of pectin effectively reduced the particle size of HA. However, the addition of pectin above 1 wt % did not contribute significantly to the densification and hardness of chicken bone-derived HA (CHA) compared with ball-milled CHA. Samples sintered at 1050 degrees C had the lowest relative density, owing to incomplete particle fusion. Increasing the sintering temperature resulted in a maximum relative density of ca. 95 % and a Vickers microhardness of 4.12 GPa for ball-milled CHA samples sintered at 1250 degrees C. Sintering temperature and ball milling were observed to play a more significant role in the densification and hardness of CHA compared with the addition of pectin.
| Item Type: | Article |
|---|---|
| Funders: | TAR UMT Internal Research Grant (UC/I/G2021-00080), Tunku Abdul Rahman University of Management and Technology, Universiti Tunku Abdul Rahman |
| Uncontrolled Keywords: | Bioceramics; Hardness; Hydroxyapatite; Pectin |
| Subjects: | T Technology > TP Chemical technology |
| Divisions: | Faculty of Engineering > Department of Mechanical Engineering |
| Depositing User: | Ms. Juhaida Abd Rahim |
| Date Deposited: | 28 Jul 2025 04:13 |
| Last Modified: | 28 Jul 2025 04:13 |
| URI: | http://eprints.um.edu.my/id/eprint/50794 |
Actions (login required)
 |
View Item |