Aun, Adam Tan Tiek and Salleh, Noordini Mohamad and Ali, Umi Fazara Md and Basirun, Wan Jefrey and Chang, Yu-Hsu and Manan, Ninie Suhana Abdul (2025) Renewable non-enzymatic copper-based surfaces for the detection of glucose, fructose, sucrose, and galactose. Journal of Food Composition and Analysis, 139. p. 107119. ISSN 0889-1575, DOI https://doi.org/10.1016/j.jfca.2024.107119.
Full text not available from this repository.Abstract
This study aims to circumvent the environmental and logistical drawbacks of disposable electrode strips by developing Cu-based sugar sensors that can be renewed for use. In this work, Cu-based sugar sensors were prepared through the electrodeposition of CuAg or lactate-templated Cu onto a carbon paste electrode (CPE) followed by electrochemical oxidation in a sodium hydroxide solution. Users can perform this process themselves by using a pre-programmed power supply and following the provided instructions. Important synthesis parameters were initially screened using experiments with a 2k factorial design to identify the most crucial factors that affect the performance of the sugar sensor. Optimization was conducted using a central composite design when necessary. An optimal lactate-templated Cu oxide-based sugar sensor with an average sensitivity of 523 mu A cm2 mM- 1 and an optimal CuAg oxide-based sugar sensor with a sensitivity of 191 mu A cm2 mM- 1 are obtained. Cyclic voltammetry (CV) analysis revealed that the oxidation rate of glucose on CuAg and lactate-templated Cu oxide-based sugar sensors is limited by surface kinetics. Electrochemical impedance spectroscopy (EIS) revealed that increasing glucose concentration in the electrolyte causes a decrease in charge transfer resistance (Rct). A higher glucose level results in better electron transfer and therefore a higher proportional current. Field emission scanning electron microscopy (FESEM) revealed that both CuAg and lactate-templated Cu oxide-based sugar sensors produced under optimized conditions also have better active material coverage and more uniquely shaped nanostructures. Energy-dispersive X-ray spectroscopy (EDX) analysis revealed that both the optimal CuAg oxide-based sugar sensor and the lactate-templated Cu oxide-based sugar sensor have a higher oxygen-to-copper ratio, which could positively influence their catalytic properties. The current density of both sensor types was found to decline over a period of 10 days. The CuAg oxide-based sugar sensor suffered an average drop of 27.10% in current density and lactate-templated Cu oxide suffered an average drop of 31.4% in current density. Additionally, when subjected to a constant potential of 0.5 V in a 6.04 mM glucose solution for 12 hours, both sensors displayed a significant decline in current density, 40.3 % for the CuAg oxide-based sugar sensor and 45.0 % for the lactate-templated Cu oxide -based sugar sensor. However, the sugar sensors can be renewed easily after each use, circumventing the issue of electrode stability.
| Item Type: | Article |
|---|---|
| Funders: | Fundamental Research Grant Scheme, Malaysia Ministry of Higher Education (FRGS/1/2020/STG04/UM/02/3) |
| Uncontrolled Keywords: | Copper-based; Sugar sensor; Non-enzymatic; Copper oxide |
| Subjects: | Q Science > QD Chemistry |
| Divisions: | Faculty of Science > Department of Chemistry |
| Depositing User: | Ms. Juhaida Abd Rahim |
| Date Deposited: | 12 Mar 2025 01:52 |
| Last Modified: | 12 Mar 2025 01:52 |
| URI: | http://eprints.um.edu.my/id/eprint/47780 |
Actions (login required)
 |
View Item |