Ibrahim, R.; Omar, M. A.; Goh, W. C.; Mohamad, M.; Muhamad, S.; Yahya, N. A.; Radzi, Z.; Abu Kasim, N.H. (2006) Fabrication of 316L stainless steel parts by injection moulding for biomedical application using a novel binder. In: 3rd Kuala Lumpur International Conference on Biomedical Engineering 2006, 2006, Kuala Lumpur.
This is the latest version of this item.
|PDF [error in script] |
Download (43Kb) | Preview
This paper focuses on the usage of a novel binder system base on palm oil product to produce sintered parts of stainless steel 316L produced by vertical injection molding technique for biomedical application. The stainless steel 316L powder was mixed using z-blade mixer with the thermoplastic binder system comprising of polyethylene, paraffin wax, stearic acid and palm stearin which was derived from palm oil at different volume percent (%). The feedstock then was studied in term of viscosity and shear rate using capillary rheometer. The feedstock was molded using vertical injection molding machine. After molding, the green molded part was immersed into the solvent to extract part of the binder system followed by sintering under vacuum atmosphere at the temperature of 1360 degrees C. The physical and mechanical properties of the sintered part such as density, hardness, shrinkage, ultimate tensile strength and elongation were measured. Biocompatibility study of in vitro test using cell osteosarcoma MG-63 was observed and discussed.
|Item Type:||Conference or Workshop Item (Paper)|
|Additional Information:||Associate Prof. Dr. Noor Hayaty Binti Abu Kasim Department of Conservative Dentistry, Faculty of Dentistry Building, University of Malaya, 50603 Kuala Lumpur, MALAYSIA http://www.researcherid.com/rid/B-9275-2010|
|Uncontrolled Keywords:||Binder System; Palm Stearin; Stainless Steel; 316l; Injection Molding; Self-Repair; Culture-Conditions; Composite Resin; Dental Pulp Stem Cell; Functionally Graded Design; Multi Layered Post; Functionally Graded Dental Post; Soft Skills; Clinical Pairing; Dental Pulp Stromal Cells; Long-Term Expansion|
R Medicine > R Medicine (General)
R Medicine > RK Dentistry
R Medicine > RK Dentistry > Oral surger
|Divisions:||Faculty of Dentistry > Dept of Conservative Dentistry|
|Depositing User:||Associate Prof. Dr. Noor Hayaty Abu Kasim|
|Date Deposited:||25 Jan 2012 09:39|
|Last Modified:||25 Jan 2012 09:39|
Available Versions of this Item
- Fabrication of 316L stainless steel parts by injection moulding for biomedical application using a novel binder. (deposited 06 Jan 2012 09:12)
- Fabrication of 316L stainless steel parts by injection moulding for biomedical application using a novel binder. (deposited 25 Jan 2012 09:39)[Currently Displayed]
Citations0 times in Scopus | 0 times in Web of Science
Actions (For repository staff only: Login required)