Al-Ruqeishi, M.S. and Nor, R.M. and Amin, Y.M. and Al-Azri, K. (2017) Direct growth and photoluminescence of silicon nanowires without catalyst. Arabian Journal of Chemistry, 10. S2025-S2031. ISSN 1878-5352, DOI https://doi.org/10.1016/j.arabjc.2013.07.032.

Full text not available from this repository.
Official URL: http://dx.doi.org/10.1016/j.arabjc.2013.07.032

Abstract

One-dimensional (1D) silicon nanowires (SiNWs) were fabricated on catalyst free Si (1 0 0) substrate using a thermal evaporation method. Based on SVLS growth mechanism, the obtained SiNWs were 30 to 265 nm in diameter and 1.7 μm to several tens of microns in length. It was found that the presence of graphite powder only is enough to accomplish growth. A systematic study of how the growth conditions, such as the Ar carrier gas flow rate, and the growth time was performed. There are five resultant PL peaks: two blue emission peaks 465 nm (2.67 eV) and 482 nm (2.57 eV) and two green bands centered at 502 nm (2.47 eV) and 526 nm (2.36 eV) and one ultraviolet emission peak at 350 nm (3.54 eV). The theory behind these emissions was discussed.

Item Type: Article
Funders: UNSPECIFIED
Uncontrolled Keywords: Si nanowires; SVLS growth mechanism; Thermal evaporation
Subjects: Q Science > Q Science (General)
Q Science > QC Physics
Divisions: Faculty of Science > Department of Physics
Depositing User: Ms. Juhaida Abd Rahim
Date Deposited: 18 Sep 2018 02:34
Last Modified: 18 Sep 2018 02:34
URI: http://eprints.um.edu.my/id/eprint/19239

Actions (login required)

View Item View Item