Electrodeposition of quaternary alloys in the presence of magnetic field.

Ebadi, M.; Basirun, W.J.; Alias, Y.; Mahmoudian, M. (2010) Electrodeposition of quaternary alloys in the presence of magnetic field. Chemistry Central journal, 4. p. 14. ISSN 1752-153X

Full text not available from this repository. (Request a copy)


ABSTRACT: Electrodeposition of Ni-Co-Fe-Zn alloys was done in a chloride ion solution with the presence and absence of a Permanent Parallel Magnetic Field (PPMF). The PPMF was applied parallel to the cathode surface. The deposition profile was monitored chronoamperometrically. It was found that the electrodeposition current was enhanced in the presence of PPMF (9 T) compared to without PPMF. The percentage of current enhancement (Gamma%) was increased in the presence of PPMF, with results of Gamma% = 11.9%, 16.7% and 18.5% at -1.1, -1.2 and -1.3 V respectively for a 2400 sec duration. In chronoamperometry, the Composition Reference Line (CRL) for Ni was around 57%, although the nobler metals (i.e. Ni, Co) showed anomalous behaviour in the presence of Zn and Fe. The anomalous behaviour of the Ni-Co-Fe-Zn electrodeposition was shown by the Energy Dispersive X-Ray (EDX) results. From Atomic Force Microscopy (AFM) measurements, it was found that the surface roughness of the Ni-Co-Fe-Zn alloy films decreased in the presence of a PPMF.

Item Type: Article
  1. Ebadi, M.
  2. Basirun, W.J.
  3. Alias, Y.
  4. Mahmoudian, M.
Journal or Publication Title: Chemistry Central journal
Additional Information: Department of Chemistry, Faculty of Science, University of Malaya, 50603 Kuala Lumpur, Malaysia. mehdi_2222002@yahoo.com
Uncontrolled Keywords: Electrodeposition; Permanent Parallel Magnetic Field (PPMF)
Subjects: R Medicine
Divisions: Faculty of Science > Dept of Chemistry
Depositing User: Mr. Faizal Hamzah
Date Deposited: 17 May 2011 10:42
Last Modified: 17 May 2011 10:42
URI: http://eprints.um.edu.my/id/eprint/1257

Actions (For repository staff only: Login required)

View Item